Synthesis Method of Napthoyl-thiourea Derivatives

Synthesis system of Napthoyl-thiourea DerivativesCHAPTER 3METHODOLOGYThis chapter explains briefly on the synthesis method of napthoyl-thiourea derivatives, experimental characterization techniques (CHNS, FTIR, UV-Vis, UV-F, 1H and 13C NMR, Single watch crystal roentgenogram Crystallography Analysis, XRD, TGA, SEM, CV), electro certification of napthoyl-thiourea derivatives on ITO substrate, electrical conduction measurement, IV curve characteristic, performance of radical diode and suppositional calculation via Gaussion 09 software package functions.3.1Reagents, Chemicals and SolventAll chemicals employ in this contemplate were commercially unattached and used as received without any purification step taken. Chemicals namely 1-napthanoyl chloride (C10H7COCl), ammonium thiocyanate (NH4SCN), 2-a secondopyridine (C5H6N2), 2-amino-5-chloro-pyridine (C5H5N2Cl) and 3-amino-4-methylpyridine (C6H8N2) were purchased from Sigma-Aldrich. In addition, 2-amino-5-picoline (C6H8N2) and 2- amino-3-picoline (C6H8N2) were supplied from Merck.Solvents such(prenominal) as methanol (CH3OH), dichloromethane (CH2Cl2) and dimethylsulphoxide were supplied by Merck. Other solvents used in this study namely anaesthetise (CHCl3), ethyl acetate (CH3COOCH2CH3) and hexane (C6H14) were purchased from Sigma-Aldrich. Acetonitrile (C2H3N) and diethyl ether (C4H10O) were supplied by R M chemicals. Whilst, acetone (CH3COCH3) was get downed from Fisher scientific.3.2Instrumentation and impersonation TechniquesThe infrared (IR) spectra of the synthesized entangleds were recorded on a foursomeier Transform-Infrared Spectrophotometer, Perkin Elmer Spectrum 100 in the range of 4000-400 cm-1 apply potassium commonplace (KBr) pellets. Electronic absorption spectra of the samples were recorded in the range of 200-400 nm using Shimadzu UV-Visible Spectrophotometer 1601 series in 1cm3 cuvette plot of land the electronic emission spectra were recorded in the same range by using Shimadzu UV -Fluorescence Spectrophotometer. For Single X-Ray Crystallography, the diffraction data were collected at 296.15K. The structure was solved and refined by using Olex2 resultant course of instruction and refinement package using Gauss-Newton Minimization.The 1H (400.11 MHz) and 13C (100.61 MHz) NMR spectra were recorded using Bruker Avance III 400 Spectrometer in CDCl3 as solvent and internal standard at room temperature in the range between H 015ppm and C 0200ppm, respectively. Besides, CHNS-O Analyzer Flashea 1112 series was used to determine the experimental percentage of C, H, N and S elements of the synthesized compounds. Thermogravimetric analysis was performed using PerkinElmer TGA Analyzer from 0oC to 700oC at a heating rate of 10oC/min under nitrogen atmosphere. Analytical prune-layer chromatography (TLC) was carried out on precoated plate of TLC Silica Gel 60 F254 (Merck) and spots were visualized with ultraviolet swingy. The X-ray Diffraction (XRD) analysis was perform ed using Rigaku MiniFlexll from 3-80.The technique cyclic voltammetry was performed using Electrochemical Impedence Spectroscopy (EIS) PGSTAT302 with three-electrode cell consisting of a polished Pt rod working electrode, Pt discus counter electrode and AgCl reference electrode. The solutions were 10-3 M in electroactive material and 0.1 M supporting electrolyte, sulphuric acid. Electrochemical opposition Spectroscopy (EIS) PGSTAT302 was used to coat the synthesized compounds on the ITO thin film by using electrochemistry method. EIS was used to study the oxidation and reduction state of the element of the synthesized compounds. The surface morphology of the final synthesised compounds in the form of powder and thin films were scanned by JSM 6360 Joel Scanning Electron Microscopy (SEM) with accelerated voltage 20 kV and magnification from 2000 until myriad The electrical conductivity of the thin film was careful in the dark conditions by using Four-Point test and LI-200 Pyrano meter Sensor with LI-1400 Data Logger while Keithley 4200 SCS Semiconductor Characterization System and try Station were used for efficiency determination and OLED parameters were evaluated from IV curve. The performance as Diode was performed by using D2 Power add GP-430D. Last but not least, the experimental result were proven by using ab initio quantum mechanically skillful evaluation at the theoretical level of DFT B3LYP/6-31G (d,p). The physical parameters such as dipole moment, energy chevron gap (HOMO and LUMO) and Mulliken Charges Bond length were calculated using Natural Bond Orbital Theory at the same theoretical level.3.3General Research DesignIn this study, the methodology is divided into four parts. Firstly, this inquiry started with the synthesis napthoyl substructure of thiourea derivative. numberly, all the synthesized compounds were characterized by using elemental analysis, typical spectroscopic and analytical techniques and electrochemical analysis. Next, the synthesized compounds were deposited on the ITO substrate as a thin film by using electrochemical deposition method. The conductivity and performance of the synthesized compounds as OLED were evaluated. Lastly, the experimental data were compared with the theoretical calculation by using Gaussion 09 software package. Figure 3.1 shows the schematic diagram of the experimental flow chart.3.4Synthetic ApproachThe synthetic approach to obtain the compounds of interest is shown in Scheme 3.2. Thiourea derivatives (15) were prepared by using 1-naphthoyl chloride as starting material. The confection of 1-napthhoyl chloride, an equimolar measuring of ammonium thiocyanate and designated amines (3-methylpyridin-2-amine, 6-methylpyridin-3-amine, 5-methylpyridin-2-amine, pyridine-2-amine and 5-chloropyridin-2-amine) in acetone was put at reflux with constant stirring for around ca. 10 hours. After completion, the reaction mixture was cooled to room temperature before it was then filtered. Th e off-white precipitate was removed and the separate was added to some ice blocks. The precipitate was crystallised from hot acetone to afford crystals of the title compounds (15).Scheme 3.2The frequent overview of the synthetic pathway applied in this study3.5Experimental Section3.5.1Synthesis of N-((3-methylpyridin-2-yl)carbamothioyl)-1-naphthamide (1)A solution of 1-napthanoyl chloride (1.5ml, 1mol) with the equimolar amount of ammonium thiocyanate (0.76g, 1mol) in ca. 50ml acetone in 100ml two-necked round-bottom flask. The reaction mixture was put at reflux with continuous stirring for ca. 5 hours. Then, a solution of 6-methylpyridin-3-amine (1.07g, 1mol) in ca. 50ml acetone was added to the reaction mixture and was put at reflux with continuous stirring for ca. 7 hours. The progress of the reaction was monitored with TLC (Hexane DCM 32). Once the reaction completed the reaction mixture was cooled to room temperature and filtered into a beaker containing some ice cubes. The r esulting baseless brown precipitate obtained, recrystallized from hot acetone to afford the title compound (1).3.5.2Synthesis of N-((5-metylpyridin-2-yl)carbamothioyl)-1-naphtamide (2)The title compound 2, (2.33g, 96%) obtained as light scandalmongering logical solid was prepared from 1-napthanoyl chloride (1.5ml, 1mol), ammonium thiocyanate (0.76g, 1mol) and 3-methylpyridin-2-amine (1.07g, 1mol) in the panache as describe above.3.5.3Synthesis of N-((3-metylpyridin-2-yl)carbamothioyl)-1-naphtamide (3)The title compound 3, (2.66g, 98%) obtained as light yellow crystalline solid was prepared from 1-napthanoyl chloride (1.5ml, 1mol), ammonium thiocyanate (0.76g, 1mol) and 5-methylpyridin-2-amine (1.07, 1mol) in the manner as describe above.3.5.4Synthesis of N-(pyridin-2-ylcarbamothioyl)-1-naphthamide(4)In a manner similar to that described above 3, the title compound 4, (0.88g, 45%) obtained as light yellow crystalline solid was prepared from 1-napthanoyl chloride (1.5ml, 1mol), am monium thiocyanate (0.76g, 1mol) and pyridin-2-amine (0.94g, 1mol).3.5.5Synthesis of N-((5-chloropyridin-2-yl)carbamothioyl)-1-naphthamide(5)The title compound 5, (1.97g, 87%) obtained as light yellow crystalline solid was prepared from 1-napthanoyl chloride (3ml, 1mol), ammonium thiocyanate (0.76g, 9.95mmol) and 5-chloropyridin-2-amine (1.28, 1mol) in the manner as describe above.3.6Electrodeposition of Naptoyl-Thiourea Derivatives on ITO substrateThe ITO substrates were used as working electrode was firstly cleaned with distilled water, detergent and acetone by using unhearable cleaner. All the synthesized compounds (15) were deposited on the ITO substrates by electrochemistry method by using Electrochemical Impendance Spectroscopy (EIS) PGSTAT302. By using the GPES method software, cyclic voltammetry (staircase) method was set to be in normal procedure. The depositions of the compounds were done in a mixture of compound dissolved in 45ml acetonitrile (10-3 M) and 5ml sulphuric a cid (10-3 M) which act as supporting electrolyte .The cyclic of the process were set in Table 3.1 below. Figure 3.1 represent the arrangement layers of ITO/napthoyl-thiourea thin film. While, scheme 3.3 shows the boilers suit methodology for organic light emitting diode (OLED) formation and characterization.Table 3.1 Procedure set for electrodeposition processNo of scan5Start potential (V)0First Vertex Potential (V)0Second Vertex Potential (V)3Step Potential (V)0.01Scan Rate (Vs-1)0.05Figure 3.1The arrangement layers of ITO/napthoyl-thiourea thin film (1a5a)3.7Electrical Conductivity MeasurementFour point probe was used to determine the conductivity of the thin film. The planing machine resistivity of the films was measured with complete four probing system that consists of the Jandel prevalent analyse combined with a Jandel RM3 Test Unit (Figure 3.2). In this study, the electrical conductivity of thin film was measured in dark condition to see its tendency to be applied as orga nic diode. Four probes were aligned and lowered onto the sample. The two outer probes supplied a voltage diversity that drives a current by dint of the film while the two inner probes pick up a voltage difference.Figure 3.2Jandel Universal Probe and RM3 Test UnitThe sheet resistances (resistivity) for the thin films are shown in Equation 3.1 below. The unit of sheet resistance is ohms per square (-/sq) Rs = 4.532 x V / I (Equation3.1)Where Rs = sheet resistance4.532 = correction factor V = voltage measured I = current appliedThe electrical conductivity can be headstrong which it is the reciprocal (inverse) of the electrical resistivity, as shown in Equation 3.2. The unit of electrical conductivity is ohm-1 m-1 (--1 m-1) = Siemens m-1 (Sm-1). = 1 / Rs(Equation 3.2)Where, = electrical conductivityRs = sheet resistivity3.8IV Curve CharacteristicThe IV curves of the 1a5a were measured by using Keithley 4200 SCS Semiconductor Characterization System and Probe Station (Figure 3.3). I n this study, ITO substrate act as hole collecting layer (anode) while napthoyl-thiourea derivatives act as hole and electron carriers. The coated ITO substrates were hide with low work function metal which is aluminuim which act as cathode.Figure 3.3Semiconductor Characterization System and Probe StationThe I-V curve shows the relationship between the currents and voltages gradient associated with the different current terminal (anode and cathode) of the diode. The obtained curve displays the prior current, reverse current, knee voltage and breakdown voltage of the diode.3.9Performance as DiodeThe performances of 1a5a as organic diode were tested by using D2 Power Supply GP-430D (Figure 3.4) under dark condition with difference voltagesin the range 15V to 30V.Figure 3.4D2 Power Supply GP-430D